| Study on Thermal Barrier Coatings of Different Infrared NDT Method |
| CHANG Lei,WANG Yi |
| AVIC Changcheng Institute of Metrology and Measurement, Beijing 100095, China |
|
|
|
|
Abstract Infrared thermal NDT methods for debonding engine blade thermal barrier coating structure of crack, back blind holes and other defects is researched and different excitation sources of different defect resolution are studied. For thermal barrier coating debonding, back blind hole defects using nondestructive testing flash excitation comparative study, for thermal barrier coating cracks using flash, nondestructive testing ultrasonic excitation source comparative study. The results show that the two excitation sources are able to complete the thermal barrier coating defects infrared nondestructive testing, detection method continuous flash excitation source for debonding, the ability to distinguish a blind hole defects back stronger, is detected by ultrasound excitation methods for detecting cracks stronger.
|
|
|
|
|
|
|
|
［1］陈学定, 韩文政. 表面涂层技术［M］. 北京: 机械工业出版社, 1994.
［2］张九渊. 表面工程与失效分析［M］. 杭州: 浙江大学出版社, 2005.
［3］王庆胜. 航空发动机涡轮叶片缺陷检测中的关键技术研究［D］. 西安: 西北工业大学, 2005.
［4］Subramanian R, Kulkarni A A.Methodologies for non-destructive quantification of thermal barrier coating temperature on service run parts［P］. US2007/0076845 A1,2007.
［5］陆佳佳,飞机涡轮发动机叶片红外探伤技术研究［D］. 成都: 电子科技大学, 2007.
［6］孙国栋,吴云峰,叶玉堂,等.涡轮叶片红外热波无损检测技术研究［J］.红外,2009,30（6）: 39-43. |
|
|
|
2015, Vol. 36 